EVAPORATION OF CADMIUM FROM MELTS WITH CRYSTALLIZATION OF IMPURITIES

The continuous weighing technique has been used for determination of cadmium evaporation degree (α) and rate (V) from binary alloys with nickel, copper and silver (2 wt.% each) at the temperature of 400–500 °C and the pressure of 13–2660 Pa with liquidus line transition from the liquid solution range to the impurity crystallization range under the isothermal conditions. The αand V change curves in time are characteristic for the impurity accumulation processes in the residue and the growing effect of the diffusion factor of more volatile component – cadmium supply to the evaporation surface. When the system passes the liquidus line, the V(τ) curves show a specific kink with V value decrease caused by the evaporation mechanism change. The cadmium evaporation rate in the two-phase field of coexistence cadmium intermetallic compound and liquid solutions on its basis is comparable to that from homogeneous alloy and it is admissible in the process technology.

1. Любман Л.Я. Непрерывное рафинирование чернового цинка: Автореф. дис. ... канд. техн. наук. Алма-Ата: ИМиО АН КазССР, 1977.

2. Назарбеков К.Т., Исакова Р.А., Хобдабергенов Р.Ж.,Нестеров П.В. // Компл. использ. минер. сырья. 1983. № 2. С. 38—42.

3. Пазухин В.А., Фишер А.Я. Вакуум в металлургии. М.: Металлургия, 1956.

4. Храпунов В.Е., Исакова Р.А., Жунусова Г.Ж. и др. // Изв. вузов. Цв. металлургия. 2003. № 5. С. 4—10.

5. Володин В.Н., Храпунов В.Е. // Компл. использ. минер. сырья. 2007. № 5. С. 44—51.

6. Диаграммы состояния двойных металлических систем / Под ред. Н.П. Лякишева. М.: Машиностроение, 1996. Т. 1.

7. Вол А.Е., Каган И.К. Строение и свойства двойных металлических систем. М.: Наука, 1979.

8. Рузахунова Г.С., Володин В.Н., Храпунов В.Е. и др. // Компл. использ. минер. сырья. 2010. № 1. С. 56—63.

9. Володин В.Н., Храпунов В.Е., Рузахунова Г.С. Марки И.А. // Журн. физ. химии. 2011. Т. 85, № 11. С. 2191—2193.