Effect of bismuth and lead on phase composition and structure of Al—5%Si—4%Cu—4%Sn alloy

The article focuses on the actual problem of creating economically alloyed antifriction aluminum alloys doped with low-melting metals. It was found in earlier experiments that an alloy containing about 5 % Si, 4% Cu and 6 % Sn (wt.%) has a balanced complex of technological and physicomechanical properties. Due to the high cost of tin, this paper considers the possibility of reducing its concentration to 4 %, and its partial replacement by other low-melting metals, such as bismuth and lead. Thermodynamic calculations (in the Thermo-Calc program) including the construction of polythermal and isothermal sections are used to study the joint and separate influence ofthese elements on the phase composition of the Al—5%Si—4%Cu—4%Sn alloy. It is shown that the addition of lead and bismuth leads to the appearance of an extensive area of fluid separation, and therefore their total concentration should not exceed 1—2 %. The phase composition and microstructure ofthe Al—5%Si—4%Cu—4%Sn—0,5%Pb—0,5%Bi alloy were studied using scanning electron microscopy and micro X-ray spectral analysis. It was found that in the cast state, low-melting metals are evenly distributed in the structure of the alloy, and in terms of the combination of properties, the experimental aluminum alloys surpass the BrO4Z4S17 antifriction bronze. Heat treatment mode T6 leads to a significant increase in the hardness of the experimental alloy. However, in the process of heating for quenching at 500 °C, local fusion of the low-melting component occurs, which leads to deterioration of the microstructure upon re-crystallization and, as a result, causes alloy embrittlement.

1. Zolotorevskii V.S., Belov N.A. Metallurgy of foundry aluminum alloy. Moscow: MISIS, 2005 (In Russ.).

2. Polmear I.J. Light metals: From traditional alloys to nanocrystals. 4th ed. Amsterdam: Elsevier, 2006.

3. Kaufman J. Gilbert, Rooy Elwin L. Aluminum alloy castings: Properties, processes, and applications. Materials Park. ASM International, 2004.

4. Belov N.A., Gershman E.I., Gershman I.S., Goryacheva I.G., Zagorskij D.L., Kotova E.G., Mahovskaya Yu.Yu., Mezrin A.M., Mironov A.E., Murav’eva T.I., Sachek B.Yа., Stolyarova O.O., Torskaya E.V. Aluminum alloys of antifriction designation. Moscow: MISIS, 2016 (In Russ.).

5. Mironov A.E., Gershman I.S., Kotova E.G., Ovechkin A.V, Gershman E.I., Zheleznov M.M. Properties of new cast antifrictional aluminum alloys. Russ. Eng. Res. 2017. Vol. 37. No. 1. P. 37—39.

6. Stolyarova O.O., Muravyeva T.I., Zagorskiy D.L., Gubenko M.M. Investigation of the surface of antifriction Al— Cu—Si—Sn—Pb aluminum alloys. J. Surf. Invest.: X-ray, Synchrotron and Neutron Techniques. 2017. Vol. 11. No. 4. P. 832—839.

7. Costa T.A., Dias M., Freitas E.S., Casteletti L.C. The effect of micro structure length scale on dry sliding wear behavior of monotectic Al—Bi—Sn alloys. J. Alloys and Compd. 2016. Vol. 689. P. 767—776.

8. Bertelli F., Freitas E.S., Cheung N., Arenas M.A., Conde A., Juan de Damborenea, Garcia A. Microstructure, tensile properties and wear resistance correlation on directionally solidified Al—Sn (Cu, Si) alloys. J. Alloys and Compd. 2017. Vol. 695 P. 3621—3631.

9. Belov N.A., Akopyan T.K., Gershman I.S., Stolyarova O.O., Yakovleva A.O. Effect of Si and Cu additions on the phase composition, microstructure and properties of Al—Sn alloys. J. Alloys and Compd. 2017. Vol. 695. P. 2730—2739.

10. Belov N.A., Mikhailina A.O., Alabin A.N., Stolyarova O.O. Theoretical and experimental study of the Al— Si—Cu—Sn phase diagram in the range of aluminum alloys. Metal Science and Heat Treatment. 2016. No. 4. P. 195—201.

11. BertelliF., Brito C., Ferreira I.L., ReinhartG., Nguyen-ThiH., Mangelinck-Noel N., Cheung N., Garcia A. Cooling thermal parameters, microstructure, segregation and hardness in directionally solidified Al—Sn—(Si,Cu) alloys. Mater. and Design. 2015. Vol. 72. Р. 31—42.

12. Lyakishev N.P. (Ed.). State diagrams of double metal systems: Handbook. Vol. 1. Moscow: Mashinostroenie, 1996 (In Russ.).

13. Mondol’fo L.F. Structure and properties of aluminum alloys. Moscow: Metallurgiya, 1979 (In Russ.).

14. Pilote L., Gheribi A. E., Chartrand P. Study of the solubility of Pb, Bi and Sn in aluminum by mixed CALPHAD/ DFT methods: Applicability to aluminum machining alloys. Calphad. 2018. Vol. 61. P. 275—287.

15. Kaban I., Kohler M., Ratke L., Hoyer W., Mattern N., Eckert J., Greer A.L. Interfacial tension, wetting and nu-cleation in Al—Bi and Al—Pb monotectic alloys. Acta Mater. 2011. Vol. 59. Р. 6880—6889.

16. Costa T.A., Freitas E.S., Dias M., Brito C., Cheung N., Garcia A. Monotectic Al—Bi—Sn alloys directionally solidified: Effects of Bi content, growth rate and cooling rate on the microstructural evolution and hardness. J. Alloys and Compd. 2015. Vol. 653. Р 243—254.

17. Dai R., Zhang J.F., Zhang S.G., Li J.G. Liquid immiscibility and core-shell morphology formation in ternary Al—Bi— Sn alloys. Mater. Charact. 2013. Vol. 81. Р. 49—55.

18. Kamal M., El-Bediwi A., Hameed M.M. Rapid quenching of liquid aluminum-indium-bismuth alloys. Int. J. Eng. Technol. 2014. Vol. 14. No. 4. Р. 23—32.

19. Petzow G., Effenberg G. Ternary alloys: A comprehensive compendium of evaluated constitutional data and phase diagrams. (Editors). Wiley-VCH. 1990. Vol. 3.

20. Thermodynamic calculations. www.thermocalc.com (In Russ.) (accessed: 04.07.2017).

21. Mironov A.E., Gershman I.S., Ovechkin A.V, Gershman E.I. The interrelation of the runin ability of bronzes and aluminum- based antifricrion alloys with their mechanical properties and degree of alloying. J. Frict. Wear. 2016. Vol. 37. No. 1. P. 23—26.

22. Osintsev O.E., Fedorov V.N. Copper and copper alloys. Domestic and foreign grades: Handbook. Moscow: Mashinostroenie, 2004 (In Russ.).