RESOURCES OF A NEW COLD UPSETTING METHOD FOR MAGNESIUM PLASTIFICATION
https://doi.org/10.17073/0021-3438-2017-1-53-60
Abstract
The study proposes a new method for the cold deformation of cast magnesium. It consists in upsetting using a under lateral pressure. The bar is first placed into a holder made of ductile material, and then into a container. The punch mounted in a container with a gap acts on the blank. Under the press force, the metal contained in the holder flows through the gap and creates a pressure. This increase the level of compressive stresses thus improving magnesium ductility. Deformation tests of cast magnesium specimens were made that showed that the nondestructive reduction of cross-sectional area could be increased from 12–18 to 60–70 %. Such an increase in ductility makes it possible to produce deformed magnesium bars without heating. The method for easier removal of bars from holders after deformation was provided. It was determined that the process could be carried out at moderate upsetting pressures of 820– 830 MPa. This is acceptable for modern tool materials.
About the Authors
B. I. Kamenetskii
Institute of Metal Physics n.a. M.N. Mikheev of Ural Branch of Russian Academy of Sciences (IMP UB RAS)
Russian Federation
Russian Federation
Cand. Sci. (Tech.), leading researcher, Laboratory of Strength,
620990, Ekaterinburg, S. Kovalevskoi str., 18
Yu. N. Loginov
Ural Federal University (UrFU) n.a. the first President of Russia B.N. Yeltsin
Russian Federation
Russian Federation
Dr. Sci. (Tech.), prof., Metallurgical Department,
620002, Russia, Ekaterinburg, Mira str., 19
N. A. Kruglikov
UrFU;
Institute of Metal Physics IMP UB RAS
Russian Federation
Russian Federation
Cand. Sci. (Phys.-Math.), associate prof. of the Department of physical methods of quality control;
senior researcher of the Laboratory of Strength
References
1. Powell B.R., Krajewski P.E., Luo A.A. Magnesium alloys for lightweight powertrains and automotive structures. In: Materials, design and manufacturing for lightweight vehicles. Cambridge: Woodhead Publishing Limited, 2010. P. 114—173.
2. Barnett M.R. Forming of magnesium and its alloys. In: Fundamentals of magnesium alloy metallurgy. Cambridge: Woodhead Publishing Limited, 2013. P. 197—231.
3. Nave M.D., Barnett M.R. Microstructures and textures of pure magnesium deformed in plane-strain compression. Scr. Mater. 2004. Vol. 51. Iss. 9. P. 881—885.
4. Loginov Yu.N., Burkin S.P., Sapunzhi V.V. Izuchenie uprochneniya i razuprochneniya magniya s uchetom anizotropii svoistv [The study of hardening and softening of magnesium with anisotropic properties]. Izvestiya vuzov. Tsvetnaya metallurgiya. 1999. No. 6. P. 42—46.
5. Loginov Yu.N., Pyshmintsev I.Yu., Popov A.A., Lunina T.G. Svoistva pressovannogo granulirovannogo magnievogo splava so sverkhmelkozernistoi strukturoi [The properties of compacted granular magnesium alloy with ultrafine structure]. Izvestiya vuzov. Tsvetnaya metallurgiya. 1998. No. 6. P. 41—44.
6. Klimanek P., Potzsch A. Microstructure evolution under compressive plastic deformation of magnesium at different temperatures and strain rates. Materials Sci. Eng. A. 2002. Vol. 324. P. 145—150.
7. Qiao X.G. , Zhao Y.W., Gan W.M., Chen Y., Zheng M.Y., Wu K., Gao N., Starink M.J. Hardening mechanism of commercially pure Mg processed by high pressure torsion at room temperature. Mater. Sci. Eng. A. 2014. Vol. 619. P. 95—106.
8. Volkov A.Yu., Kliukin I.V. Improving the mechanical properties of pure magnesium through cold hydrostatic extrusion and low-temperature annealing. Mater. Sci. Eng. A. 2015. Vol. 627. P. 56—60.
9. Kamenetskii B.I., Loginov Yu.N., Kruglikov N.A. Vliyanie uslovii bokovogo podpora na plastichnost’ magniya pri kholodnoi osadke [Influence of lateral stress conditions on the plasticity of magnesium in the cold upsetting]. Tekhnologiya legkikh splavov. 2012. No. 1. P. 86—92.
10. Kamenetskii B.I., Loginov Yu.N., Volkov A.Yu. Metody i ustroistva dlya povysheniya plastichnosti khrupkikh materialov pri kholodnoi osadke s bokovym podporom [Methods and apparatus for improving the ductility of brittle materials by cold upsetting with lateral stress]. Zagotovitel’nye proizvodstva v mashinostroenii. 2013. No. 9. P. 15—22.
11. Storozhev M.V., Popov E.A. Teoriya obrabotki metallov davleniem [Theory of metal forming]. Moscow: Mashinostroenie, 1977.
12. Narayanasamy R., Sathiyanarayanan S., Ponalagusamy R. A study on barrelling in magnesium alloy solid cylinders during cold upset forming. J. Mater. Process. Technol. 2000. Vol. 101. Iss. 1—3. P. 64—69.
13. Mathis K., Trojanova Z., Lukac P., Caceres C.H., Lendvai J. Modeling of hardening and softening processes in Mg alloys. J. Alloys Compd. 2004. Vol. 378. P. 176—179.
14. Kruglikov N.A., Loginov Yu.N., Kamenetskii B.I., Savrai R.A., Dolmatov A.V., Klyukin I.V., Volkov A.Yu. Mikrostruktura i mekhanicheskie svoistva litogo magniya [The microstructure and mechanical properties of cast magnesium]. Liteishchik Rossii. 2013. No. 8. P. 17—22.
15. Matsumoto R., Kubo T., Osakada K. Fracture of magnesium alloy in cold forging. CIRP Ann. Manuf. Technol. 2007. Vol. 56. Iss. 1. P. 293—296.
16. Kamenetskii B.I., Sokolov A.L., Volkov A.Ju. Kruglikov N.A. Sposob osadki tsilindricheskikh zagotovok iz khrupkikh i maloplastichnykh materialov [Method of upsetting fragile and low-plasticity cylindrical blanks]: Pat. 2501624 (RF). 2013.
Review
For citations:
Kamenetskii B.I., Loginov Yu.N., Kruglikov N.A. RESOURCES OF A NEW COLD UPSETTING METHOD FOR MAGNESIUM PLASTIFICATION. Izvestiya. Non-Ferrous Metallurgy. 2017;(1):53-60. (In Russ.) https://doi.org/10.17073/0021-3438-2017-1-53-60
Views:
680
Email this article 