THE EFFECT OF ENVIRONMENT PH ON ANODIC BEHAVIOR OF ZN55AL ALLOY DOPED WITH SCANDIUM

The anodic behavior of Zn55Al alloy doped with scandium has been studied. The scandium content dependence of the Zn55Al alloy corrosion potential shows the extreme character. The increase in the chloride ion concentration in the electrolyte reduces the corrosion potential. When doping element content grows in the alloys, pitting and repassivation potentials are shifted to the positive area, and when chloride ion concentration grows, the potentials are shifted to the negative area over the entire range of environment pH. Zn55Al alloy corrosion rate decreases 2–3 times in doping 0,005–0,05 wt.% scandium. Thus the alloys of such composition can be recommended as anode coating for corrosion protection of steel structures, components, and constructions.

1. Кечин В.А., Люблинский Е.Я. Цинковые сплавы. М.: Металлургия, 1986.

2. Обидов З.Р., Ганиев И.Н. Анодные защитные цинк-алюминиевые покрытия с элементами II группы. Германия: Lap Lambert Acad. Publ., 2012.

3. Обидов З.Р., Ганиев И.Н., Алиев Д.Н., Ганиева Н.И. // Журн. прикл. химии. 2010. Т. 83, № 4. С. 962—965.

4. Обидов З.Р., Ганиев И.Н. Анодное поведение и окисление сплавов систем Zn5Al—ЩЗМ и Zn55Al—ЩЗМ. Германия: Lap Lambert Acad. Publ., 2011.

5. Ганиев И.Н., Умарова Т.М., Обидов З.Р. Коррозия двойных сплавов алюминия с элементами периодической системы. Германия: Lap Lambert Acad. Publ., 2011.

6. Колотыркина Я.М. Металл и коррозия. М.: Металлургия, 1985.

7. Улиг Г.Г., Реви Р.У. Коррозия и борьба с ней. Введение в коррозионную науку и технику. Л.: Химия, 1989.

8. Ганиев И.Н., Назаров Х.М., Одинаев Х.О. Сплавы алюминия с редкоземельными металлами. Душанбе: Мао- риф, 2004.