INVESTIGATION OF GROW-BACK DURING ROLLING ON LONGITUDINAL V-SHAPE MILL
https://doi.org/10.17073/0021-3438-2014-4-36-41
Abstract
There was investigated influence of morphology of graded waste chips from brasses L63 on properties of bars and wires obtained by means of chipless shaping. For research particles of chips were divided on 3 types: spiral, flaked and sawing. Any one of them was heated to temperature 450±5 °С and briquetted on the forgemaster. Afterwards briquettes were heated to temperature of 850 °C and extruded by means of direct method with resulting of bars diameters 8 and 6 mm. Herewith elongating ratios were equal to 32 and 56, correspondingly. Pressed bars were subject to drawing, as consequence diameter of wire was equal to 2 and 3 mm. Examination of bars and wire properties showed that waste chips from brasses L 63 could be raw materials during manufacturing of half-prepared products for hot extrusion and subsequent wire drawing. There was established that morphology of chips particles has a little effect on fabrication characteristics of briquettes, as well as on mechanical characteristics of pressed bars and obtained by means of drawing wire, mechanical properties of which meet demands of GOST 1066-90.
About the Authors
S. A. Mashekov
Казахский национальный технический университет (КазНТУ) им. К. Сатпаева, г. Алматы
Kazakhstan
Kazakhstan
докт.техн.наук,профессор кафедры металлургических машин и оборудования КазНТУ
050013, Казахстан, г. Алматы, ул. Сатпаева, 22
Тел.: (8-727) 257-70-69
N. T. Smailova
Павлодарский государственный университет (ПГУ) им. С. Торайгырова, Казахстан
Kazakhstan
Kazakhstan
докт.техн.наук,профессор кафедры металлургии ПГУ
140008, Казахстан, г. Павлодар, ул. Ломова, 64
Sh. A. Bekmukhanbetova
Казахский национальный технический университет (КазНТУ) им. К. Сатпаева, г. Алматы
Kazakhstan
канд.техн.наук,ст.преподаватель кафедры металлургических машин и оборудования КазНТУ
Kazakhstan
канд.техн.наук,ст.преподаватель кафедры металлургических машин и оборудования КазНТУ
E. Z. Nugman
Казахский национальный технический университет (КазНТУ) им. К. Сатпаева, г. Алматы
Kazakhstan
канд.техн.наук,ст.преподаватель кафедры металлургических машин и оборудования КазНТУ
Kazakhstan
канд.техн.наук,ст.преподаватель кафедры металлургических машин и оборудования КазНТУ
G. A. Smailova
Казахский национальный технический университет (КазНТУ) им. К. Сатпаева, г. Алматы
Kazakhstan
канд.техн.наук,ст.преподаватель кафедры металлургических машин и оборудования КазНТУ
Kazakhstan
канд.техн.наук,ст.преподаватель кафедры металлургических машин и оборудования КазНТУ
References
1. Мазур В.Л., Ноговицын А.В. Теория и технология тонколистовой прокатки. Днепропетровск: РВА «Дніпро-VAL», 2010.
2. Шевакин Ю.Ф., Кручер Н.Г. // Цв. металлы. 1997. № 5. С. 71—74.
3. Максимов Е.А. // Нац. металлургия. Оборудование. 2005. № 1. С. 22—27.
4. Boulton G., Domanti T., Gerber T., Wallace G. Strip edge shape control. Achieving profile & Flatness in Flat Products. IOM Conf. (Birmingham, Jan. 2006). Р. 57—64.
5. Максимов Е.А. // Нац. металлургия. Оборудование. 2006. № 11. С. 60—65.
6. Агеев Л.М. // Тр. 4-го Конгр. прокатчиков (Магнитогорск, 16—19 окт. 2001 г.). М.: Черметинформация, 2002. Т. 1. С. 192—197.
7. Антипин В.Г. // Бюл. Черная металлургия. 2002. № 8. С. 3—9.
8. Кулик А.Н., Юрков К.Ю., Файчак А.А., Шевченко В.В. Перспективные конструкции прецизионных станов // http://www.nbuv.gov.ua/portal/ natural/Zmmvp/2008_10/3.pdf.
9. Максимов Е.А. // Нац. металлургия. Оборудование. 2006. № 9. С. 45—51.
10. Шевакин Ю.Ф., Райков Ю.Н., Бушев А.В., Баканов М.Б. // Цв. металлы. 2000. № 2. С. 91—97.
11. Пат. № 20969 (РК). Непрерывный стан для прокатки полос из сталей и сплавов/ С.А. Машеков, Е.З. Нугман, А.С. Машекова и др. 2009.
Review
For citations:
Mashekov S.A., Smailova N.T., Bekmukhanbetova Sh.A., Nugman E.Z., Smailova G.A. INVESTIGATION OF GROW-BACK DURING ROLLING ON LONGITUDINAL V-SHAPE MILL. Izvestiya. Non-Ferrous Metallurgy. 2014;(4):36-41. (In Russ.) https://doi.org/10.17073/0021-3438-2014-4-36-41
Views:
918
Email this article 