INTERACTION OF SINTERED ALUMINIUM NITRIDE WITH MELT KF–ALF3 AT TEMPERATURE 700–800 °C
https://doi.org/10.17073/0021-3438-2014-4-25-29
Abstract
By means of continuous weighing method was investigated the kinetics of the interaction of sintered composite on the base of aluminium nitride with the molten potassium cryolite with cryolite ration (CR) 1,3 at temperatures of 700–800 °C. There was specified that at temperature 700 °C composite practically did not exposed to melt impact. Materials interact with molten salt through the stage of its oxidation in the melt of oxygen. At this, takes place besides merging of originally presented in material of oxygen-containing impurities. In the absence of an oxidizer and at concentration of dissolved in cryolite alumina, close to saturation, interaction of sintered aluminium nitride with examined melt did not observed.
About the Authors
A. Yu. Chuikin
Институт высокотемпературной электрохимии (ИВТЭ) УрО РАН, г. Екатеринбург
Russian Federation
Russian Federation
канд. хим. наук, науч. сотр. лаборатории твердооксидных топливных элементов ИВТЭ УрО РАН
(620990, г. Екатеринбург, ул. Академическая, 20).
Тел.: (343) 362-35-73.
Yu. P. Zaikov
Институт высокотемпературной электрохимии (ИВТЭ) УрО РАН, г. Екатеринбург
Russian Federation
Russian Federation
докт. хим. наук, проф., директор ИВТЭ УрО РАН.
Тел.: (343) 374-50-89.
A. R. Beketov
Уральский федеральный университет (УрФУ)
им. первого Президента России Б.Н. Ельцина, г. Екатеринбург
Russian Federation
Russian Federation
докт. техн. наук, проф., зав. кафедрой редких металлов и наноматериалов УрФУ
(620002, г. Екатеринбург, ул. Мира, 19).
Тел.: (343) 374-54-91.
References
1. Косолапова Т.Я. Тугоплавкие нитриды. Киев: Наук. думка, 1983.
2. Самсонов Г.В. Неметаллические нитриды. М.: Металлургия, 1969.
3. Горланов Е.С., Борисоглебский Ю.В., Ветюков М.М., Ахмедов С.Н. // Цв. металлы. 1992. № 1. С. 24—25.
4. Schwarzkopf P., Kieffer R. // Refractory Hard Metals. N.Y.: Macmillan Company, 1953. Р. 21.
5. Todd J.B. // J. Metals. 1981. Vol. 33, № 9. Р. 42—45.
6. Thonstad J., Fellner P., Haarberg G.M. et al. Aluminium Electrolysis. Fundamentals of the Hall-Heroult Process. 3-rd еd. Düsseldorf: Aluminium-Verlag, 2001.
7. Yang J., Hryn J.N., Davis B.R., Roy A. // Light Metals. 2004. Р. 321—326.
8. Аписаров А.П., Ткачёва О.Ю., Зайков Ю.П. Растворимость глинозема в низкотемпературных электролитах на основе калиевого криолита: Тез. докл. Ч. II. Ново-московск: РХТУ им. Д.И. Менделеева, Новомосков-ский ин-т, 2006. С. 3—4.
9. Kryukovsky V.A., Frolov A.V., Tkatcheva O.Yu. et al. // Light Metals. 2006. Р. 409—413.
10. Yang J., Hryn J.N., Krumdick G.K. // Light Metals. 2006. Р. 421—424.
11. Redkin A., Tkatcheva O., Zaikov Y., Apisarov A. // Light Metals. 2007. Р. 513—518.
12. Chartrand P., Heyrman M. // Light Metals. 2007. Р. 519—524.
13. Jiawei Wang, Yanqing Lai, Zhongliang Tian et al. // Light Metals. 2007. Р. 525—530.
14. Hongmin Kan, Zhaowen Wang , Zhongning Shi et al. // Light Metals. 2007. Р. 531—536.
15. Yang J.-H., Graczyk D.G., Wunsch C., Hryn J. // Light Metals. 2007. Р. 537—544.
16. Чуйкин А.Ю., Бекетов Д.А., Малков В.Б. и др. // Вестн. УГТУ—УПИ. Сер. химическая. Екатеринбург: УГТУ—УПИ, 2005. С. 82—86.
Review
For citations:
Chuikin A.Yu., Zaikov Yu.P., Beketov A.R. INTERACTION OF SINTERED ALUMINIUM NITRIDE WITH MELT KF–ALF3 AT TEMPERATURE 700–800 °C. Izvestiya. Non-Ferrous Metallurgy. 2014;(4):25-29. (In Russ.) https://doi.org/10.17073/0021-3438-2014-4-25-29
Views:
1004
Email this article 