Study into the effect of different energy sources on the structure and mechanical properties of EP693 nickel alloy weld joint

The paper provides the results of a study on the influence of welding types (laser, electron beam, and TIG welding) on the properties of a permanent connection made of an EP693 alloy of the Ni–Cr–W–Co–Mo system used in the production of gas turbine engine components and parts. EP367 filler wire of the Ni–Mo–Cr–Mn system was used to obtain a weld during laser and TIG welding. A comparative analysis of heating areas and power densities was performed for the welding types studied. It was established that TIG welding features by greater values of the heating area and power density in comparison with laser and electron beam welding. It was found that the type of welding affects the features of weld formation. For example, a weld is formed with the transition to knife fusion penetration in the weld root for electron beam welding, and in the form of an «hourglass» for laser welding. The analysis of the heat affected zone microstructure showed that the smallest grain size is formed during laser welding. The distribution of elements in the weld joint was analyzed. It was found that when welding with the use of filler wire, the Mo content increases and the W, Co, Al, and Ti content decreases in the weld and heat affected zone relative to the base metal. This determines the peculiarities of failure for samples obtained using the welding types studied. Samples obtained by TIG and laser welding broke along the heat affected zone on the weld reinforcement side. Samples obtained by electron beam welding broke along the weld. Mechanical tests of samples at room and elevated temperatures showed that samples obtained by laser and electron beam welding have the highest tensile strength.

1. Leyens C. Advanced materials and coatings for future gas turbine applications. In: Proceedings of the 24th International congress of the aeronautical sciences (Yokohama, Japan, 29 August—3 September 2004). P. 1—10.

2. Inozemcev A.A., Nihamkin M.A., Sandracsky V.L. Automation and regulation of aircraft engines and power plants. Systems: Textbook for student. Moscow: Mashinostroenie, 2007 (In Russ.).

3. Lomberg B.S., Ovsepyan S.V., Bakradze M.M. High-temperature deformable nickel alloys for advanced gas turbine engines and gas turbine plants. Vestnik MGTU im. N.E. Baumana. 2011. No. S2. Р. 98—103 (In Russ.).

4. Henderson M.B., Arrell D., Heobel M., Larsson R., Marchant G. Nickel-based superalloy welding practices for industrial gas turbine applications. Sci. Technol. Weld JOI. 2004. Vol. 9. Iss. 1. P. 13—21.

5. Osintsev K.A., Konovalov S.V., Glezer A.M., Gromov V.E., Ivanov Y.F., Panchenko I.A., Sundeev R.V. Research on the structure of Al2.1Co0.3Cr0.5FeNi2.1 high-entropy alloy at submicro- and nano-scale levels. Mater. Lett. 2021. Vol. 294. Art. 129717.

6. Shen Q., Kong X., Chen X. Fabrication of bulk Al—Co—Cr—Fe—Ni high-entropy alloy using combined cable wire arc additive manufacturing (CCW-AAM): Microstructure and mechanical properties. J. Mater. Sci. Technol. 2021. Vol. 74, P. 136—142.

7. Lomberg B.S., Moiseev S.A. Heat-resistant and wrought alloys for modern promising gas turbine engines. In: All materials: Encyclopedic reference book. 2007. Vol. 6. Р. 2—5 (In Russ.).

8. Sorokin L.I. Weldability of heat-resistant alloys used in aircraft gas turbine engines. Svarochnoe proizvodstvo. 1971. No 4. P. 4—5 (In Russ.).

9. Kurochko R.S. Welding and soldering of heat-resistant materials of the hot path of the GTE. Aviacionnaya promyshlennost’. 1982. No. 8. P. 4—8 (In Russ.).

10. Caron J.L., Sowards J.W. Weldability of nickel-base alloys. Compr. Mater. Process. 2014. Vol. 6. P. 151—179.

11. Qian M., Lippold J.C. Liquation phenomena in the simulated heat-affected zone of alloy 718 after multiple post weld heat treatment cycles. Welding J. 2003. Vol. 82. No. 6. P. 145—150.

12. Sashank S. Sravan, Rajakumar S., Karthikeyan R., Nagaraju D.S. Weldability, mechanical properties and microstructure of nickel based super alloys: A review. In: Proceedings of the 2nd International Conference on Design and Manufacturing Aspects for Sustainable Energy (ICMED 2020) (Hyderabad, India, July 10—12, 2020), 2020. Vol. 184. P. 1—3.

13. Ferro P., Bonollo F., Tiziani A. Laser welding of copper—nickel alloys: A numerical and experimental analysis. Sci. Technol. Weld. Joining. 2005. Vol. 10. No. 3. P. 299—310.

14. Çam G., Koçak M. Progress in joining of advanced materials. Pt. 1: Solid state joining, fusion joining, and joining of intermetallics. Sci. Technol. Weld. Joining. 1998. Vol. 3. No. 3. P. 105—126.

15. Çam G., Koçak M. Progress in joining of advanced materials. Inter. Mater. Rev. 1998. No. 43. P. 1—44.

16. Çam G., Fischer A., Ratjen R., dos Santos J. F., Koçak M. Properties of laser beam welded superalloys Inconel 625 and 718. In: Proceedings of the 7th European Conference on Laser Treatment of Materials, ECLAT’98 (Hannover, 21—23.09.1998). P. 333—338.

17. Corba C., Ferencz P., Mihăilă I. Laser welding. Nonconvent. Technol. Rev. 2018. No.4. P. 34—37.

18. Bratukhin A.G., Maslenkov S.B., Logunov A.V., Prokopinskaya S.G., Solov’ev Yu.V. Heat treatment using high-concentrated energy suppliers. Metal Sci. Heat Treatment. 1995. Vol. 37. No. 11-12. Р. 479—484.

19. Naffakh-Moosavy H., Aboutalebi M.R., Seyedein S.H., Goodarzi M., Khodabakhshi M., Mapelli, Barella S. Modern fiber laser beam welding of the newly-designed precipitation-strengthened nickel-base superalloys. Optics Laser Technol. 2014. Vol. 57. P. 12—20.

20. Hong J.K., Park J.H., Park N.K., Eom I.S., Kim M.B., Kang C.Y. Microstructures and mechanical properties of Inconel 718 welds by CO2 laser welding. J. Mater. Process. Technol. 2008. Vol. 201. No. 1. P. 515—520.

21. Chamanfar A., Mohammad J., Gholipour J., Wanjara P., Yue S. Suppressed liquation and microcracking in linear friction welded WASPALOY. Mater. Design. 2012. Vol. 36. P. 113—122.

22. Anbarasan N., Bikash Kumar Gupta, Prakash S., Muthukumar P., Oyyaravelu R., John Felix Kumar R., Jerome S. Effect of heat treatment on the microstructure and mechanical properties of inconel 718. Mater. Today: Proceedings. 2018. No. 5. P. 7716—7724.

23. Yoshinori Ono, Tetsumi Yuri, Nobuo Nagashima, Hideshi Sumiyoshi, Toshio Ogata, Naoki Nagao. High-cycle fatigue properties of Alloy718 base metal and electron beam welded joint. Phys. Procedia. 2015.Vol.67. P. 1028—1035.

24. Rautio T., Mäkikangas J., Kumpula J., Järvenpää A., Hamada A. Laser welding of laser powder bed fusion manufactured Inconel 718: Microstructure and mechanical properties. Key Eng. Mater. 2021. Vol. 883. Р. 234—241. DOI: 10.1016/j.jmrt.2021.02.020.

25. Baranov D.А., Zhatkin S.S., Nikitin V.I., Deev V.B., Nikitin K.V., Barinov А.Yu., Yudin D.M. Ensuring the strength of welded connections in laser welding of heat-resi stant dispersion-har dening nickel alloy ЭП693. Russ. J. NonFerr. Met. 2021. Vol. 62. No. 4. Р. 441—447.

26. PI 1.4.75-2000. Production instruction. Arc welding in shielding gases of structural, stainless and heat-resistant steel and alloys. Moscow: PJS «NIAT». 2000. P. 65—70 (In Russ.).

27. GOST 6996-66. Welded joints. Methods for determining mechanical properties. Moscow: Standartinform, 2008 (In Russ.).

28. Sorokin L.I. Weldability of heat resistant alloys used in aircraft gas turbine engines. Svarochnoe proizvodstvo. 1971. Vol. 4. Р. 4—5 (In Russ.)