THERMODYNAMIC MODELING OF Y2O3 INTERACTION WITH NB–SI BASED MELTS
https://doi.org/10.17073/0021-3438-2013-6-14-18
Abstract
The thermodynamic modeling of interaction of yttrium ceramic with Nb–Si based molten alloys alloyed with Ti, Cr, Hf, Al has been performed. Formation of solid HfO2 oxide is shown to be the result of such interaction, and other elements are not involved practically in the chemical interaction. It is found in the course of modeling that yttrium reduction due to ceramic dissolution in the molten metallic solution is the main mechanism of interaction. The Y content in the solution depends on the temperature, metallic phase composition, and quantity.
Keywords
About the Authors
A. K. Zaitsev
Национальный исследовательский технологический университет «МИСиС», г. Москва
Russian Federation
Russian Federation
A. O. Rodin
Национальный исследовательский технологический университет «МИСиС», г. Москва
Russian Federation
Russian Federation
B. S. Bokshtein
Национальный исследовательский технологический университет «МИСиС», г. Москва
Russian Federation
Russian Federation
I. L. Svetlov
ГНЦ «Всероссийский институт авиационных материалов» (ВИАМ), г. Москва
Russian Federation
Russian Federation
Yu. I. Folomeikin
ГНЦ «Всероссийский институт авиационных материалов» (ВИАМ), г. Москва
Russian Federation
Russian Federation
References
1. Bewlay B.P., Jackson M.R., Gigliotti. M.F.X. // Intermetallic Compounds, Principles and Practice / Eds. J.H. Westbro, R.I. Fleischer. Ames: Wiley, 2002. Vol. 3. P. 541—560.
2. Ji-Cheng Zhao, Bewley B.P., Peluso L.A. // Structural Intermetallics. 2001. P. 583—592.
3. Shi Yu Qu, Ya Fang Han, Yong Wang Kang // Sci. China Ser.: Technol. Sci. 2009. Vol. 52, № 1. Р. 37.
4. Subramanian P.R., Mendiratta M.G., Dimiduk D.M. // JOM. 1996. Vol. 48, № 1. Р. 33.
5. Jackson M.R., Bewley B.P., Rowe R.G. et al. // Ibid. Р. 39.
6. Tanaka R., Kasama A., Fujikura M. et al. // Proceedings of the International Gas Turbine Congress. Ames: Wiley, 2003. Р. 1—5.
7. Sekido N., Kimura Y., Miura S. et al. // J. Alloys Compd. 2006. Vol. 425. P. 223.
8. Gao M., Jia L., Tang X. et al. // China Foundry. 2011. Vol. 8, № 2. P. 273.
9. Ma L.M., Yuan S.N., Cui R.J. et al. // Inter. J. Ref. Met. Hard Mater. 2012. Vol. 30. P. 96.
10. Иориш В.С., Белов Г.В., Юнгман В.С. Программный комплекс ИВТАНТЕРМО для Windows и его использование в прикладных термодинамических расчетах: Препр. изд. № 8-415. М.: ОИВТ РАН, 1998.
11. Stacy D.W., Wilder D.R. // J. Amer. Ceram. Soc. 1975. Vol. 58. Р. 285—288
Review
For citations:
Zaitsev A.K., Rodin A.O., Bokshtein B.S., Svetlov I.L., Folomeikin Yu.I. THERMODYNAMIC MODELING OF Y2O3 INTERACTION WITH NB–SI BASED MELTS. Izvestiya. Non-Ferrous Metallurgy. 2013;(6):14-18. (In Russ.) https://doi.org/10.17073/0021-3438-2013-6-14-18
Views:
768
Email this article 